题名: Growth of CeO2 : Bi12SiO20 crystals in multi-position furnace(II) - Space growth experiment
作者: Zhou YF;  Wang JC;  Tang LA;  Chen NF;  Chen WC
发表日期: 2004
摘要: Ce-doped Bi12SiO20 single crystal with size of phi10mm x 40mm was successfully grown in space on board of the spacecraft Shenzhou No.3. The surface morphology of space-grown crystal is different from that of ground-grown crystal The space- and ground-grown crystals were measured by X-ray rocking curves, absorption spectra and micro-Raman spectra. The results show that the quality of Ce-deped crystal grown in space is better than that of the ground-grown one. The effect of doping on optical properties of BSO grown in space is evident in comparison with the ground-grown crystal.
刊名: JOURNAL OF INORGANIC MATERIALS
专题: 中国科学院半导体研究所(2009年前)_期刊论文

条目包含的文件

文件 大小格式
1886.pdf529KbAdobe PDF 联系获取全文


许可声明:条目相关作品遵循知识共享协议(Creative Commons)。


推荐引用方式:
Zhou, YF; Wang, JC; Tang, LA; Chen, NF; Chen, WC .Growth of CeO2 : Bi12SiO20 crystals in multi-position furnace(II) - Space growth experiment ,JOURNAL OF INORGANIC MATERIALS,MAR 2004,19 (2):283-288
个性服务
 推荐该条目
 保存到收藏夹
 查看访问统计
 Endnote导出
Google Scholar
 Google Scholar中相似的文章
 [Zhou YF]的文章
 [Wang JC]的文章
 [Tang LA]的文章
CSDL跨库检索
 CSDL跨库检索中相似的文章
 [Zhou YF]的文章
 [Wang JC]的文章
 [Tang LA]的文章
Scirus search
 Scirus中相似的文章
Social Bookmarking
  Add to CiteULike  Add to Connotea  Add to Del.icio.us  Add to Digg  Add to Reddit 
所有评论 (0)
暂无评论

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。

 

 

Valid XHTML 1.0! 版权所有 © 2007-2012  中国科学院半导体研究所  -反馈
系统开发与技术支持:中国科学院国家科学图书馆兰州分馆(信息系统部)
本系统基于 MIT 和 Hewlett-Packard 的 DSpace 软件开发