题名: Mn-AlInN: a new diluted magnetic semiconductor
作者: Majid A;  Sharif R;  Zhu JJ;  Ali A
发表日期: 2009
摘要: Mn ions have been incorporated into MOCVD grown Al1-x In (x) N/GaN thin films by ion implantation to achieve the room temperature ferromagnetism in the samples. Magnetic characterizations revealed the presence of two ferromagnetic transitions one has Curie points at similar to 260 K and the other above room temperature. In-diffusion of indium caused by the Mn implantation leads to the partition of AlInN epilayer into two diluted magnetic semiconductor sub-layers depending on the Mn concentration. The Curie temperature of 260 K is assigned to the layer having lower concentration, whereas T (c) above room temperature is assumed to be associated to the layer having higher Mn concentration.
KOS主题词: Photography--Films;  Finite volume method;  Development;  Chromium
刊名: APPLIED PHYSICS A-MATERIALS SCIENCE & PROCESSING
专题: 中国科学院半导体研究所(2009年前)_期刊论文

条目包含的文件

文件 大小格式
51.pdf489KbAdobe PDF 联系获取全文


许可声明:条目相关作品遵循知识共享协议(Creative Commons)。


推荐引用方式:
Majid A ; Sharif R ; Zhu JJ ; Ali A .Mn-AlInN: a new diluted magnetic semiconductor ,APPLIED PHYSICS A-MATERIALS SCIENCE & PROCESSING,2009 ,96(4):979-984
个性服务
 推荐该条目
 保存到收藏夹
 查看访问统计
 Endnote导出
Google Scholar
 Google Scholar中相似的文章
 [Majid A]的文章
 [Sharif R]的文章
 [Zhu JJ]的文章
CSDL跨库检索
 CSDL跨库检索中相似的文章
 [Majid A]的文章
 [Sharif R]的文章
 [Zhu JJ]的文章
Scirus search
 Scirus中相似的文章
Social Bookmarking
  Add to CiteULike  Add to Connotea  Add to Del.icio.us  Add to Digg  Add to Reddit 
所有评论 (0)
暂无评论

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。

 

 

Valid XHTML 1.0! 版权所有 © 2007-2012  中国科学院半导体研究所  -反馈
系统开发与技术支持:中国科学院国家科学图书馆兰州分馆(信息系统部)
本系统基于 MIT 和 Hewlett-Packard 的 DSpace 软件开发