题名: Influence of electron irradiation on hydrothermally grown zinc oxide single crystals
作者: Lu LW;  So CK;  Zhu CY;  Gu QL;  Li CJ;  Fung S;  Brauer G;  Anwand W;  Skorupa W;  Ling CC
发表日期: 2008
摘要: The resistivity of hydrothermally grown ZnO single crystals increased from similar to 10(3) Omega cm to similar to 10(6) Omega cm after 1.8 MeV electron irradiation with a fluence of similar to 10(16) cm(-2), and to similar to 10(9) Omega cm as the fluence increased to similar to 10(18) cm(-2). Defects in samples were studied by thermally stimulated current (TSC) spectroscopy and positron lifetime spectroscopy (PLS). After the electron irradiation with a fluence of 10(18) cm(-2), the normalized TSC signal increased by a factor of similar to 100. A Zn vacancy was also introduced by the electron irradiation, though with a concentration lower than expected. After annealing in air at 400 degrees C, the resistivity and the deep traps concentrations recovered to the levels of the as-grown sample, and the Zn vacancy was removed.
KOS主题词: Diodes, Schottky-barrier
刊名: SEMICONDUCTOR SCIENCE AND TECHNOLOGY
专题: 中国科学院半导体研究所(2009年前)_期刊论文

条目包含的文件

文件 大小格式
405.pdf516KbAdobe PDF 联系获取全文


许可声明:条目相关作品遵循知识共享协议(Creative Commons)。


推荐引用方式:
Lu, LW ; So, CK ; Zhu, CY ; Gu, QL ; Li, CJ ; Fung, S ; Brauer, G ; Anwand, W ; Skorupa, W ; Ling, CC .Influence of electron irradiation on hydrothermally grown zinc oxide single crystals ,SEMICONDUCTOR SCIENCE AND TECHNOLOGY,2008 ,23(9): Art. No. 095028
个性服务
 推荐该条目
 保存到收藏夹
 查看访问统计
 Endnote导出
Google Scholar
 Google Scholar中相似的文章
 [Lu LW]的文章
 [So CK]的文章
 [Zhu CY]的文章
CSDL跨库检索
 CSDL跨库检索中相似的文章
 [Lu LW]的文章
 [So CK]的文章
 [Zhu CY]的文章
Scirus search
 Scirus中相似的文章
Social Bookmarking
  Add to CiteULike  Add to Connotea  Add to Del.icio.us  Add to Digg  Add to Reddit 
所有评论 (0)
暂无评论

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。

 

 

Valid XHTML 1.0! 版权所有 © 2007-2012  中国科学院半导体研究所  -反馈
系统开发与技术支持:中国科学院国家科学图书馆兰州分馆(信息系统部)
本系统基于 MIT 和 Hewlett-Packard 的 DSpace 软件开发