题名: Investigation of defects in low-temperature-grown GaAs using optical transient spectroscopy
作者: Zhang YH;  Lu LW;  Zhang MH;  Huang Q;  Bao CL;  Zhou JM
发表日期: 2000
摘要: Optical transient current spectroscopy (OTCS) has been used to investigate defects in the low-temperature-grown GaAs after postgrowth rapid thermal annealing (RTA). Two samples A and B were grown at 220 degreesC and 360 degreesC on (001) GaAs substrates, respectively. After growth, samples were subjected to 30s RTA in the range of 500-800 degreesC. Before annealing, X-ray diffraction measurements show that the concentrations of the excess arsenic for samples A and B are 2.5 x 10(19) and 1 x 10(19) cm(-3), respectively. It is found that there are strong negative decay signals in the optical transient current (OTC) for the annealed sample A. Due to the influence of OTC strong negative decay signals, it is impossible to identify deep levels clearly from OTCS. For a comparison, three deep levels can be identified for sample B before annealing. They are two shallower deep levels and the so-called As-Ga antisite defect. At the annealing temperature of 600 degreesC, there are still three deep levels. However, their structures are different from those in the as-grown sample. OTC strong negative decay signals are also observed for the annealed sample B. It is argued that OTC negative decay signals are related to arsenic clusters. (C) 2000 Elsevier Science B.V. All rights reserved.
刊名: JOURNAL OF CRYSTAL GROWTH
专题: 中国科学院半导体研究所(2009年前)_期刊论文

条目包含的文件

文件 大小格式
1236.pdf135KbAdobe PDF 联系获取全文


许可声明:条目相关作品遵循知识共享协议(Creative Commons)。


推荐引用方式:
Zhang YH; Lu LW; Zhang MH; Huang Q; Bao CL; Zhou JM .Investigation of defects in low-temperature-grown GaAs using optical transient spectroscopy ,JOURNAL OF CRYSTAL GROWTH,2000,220(4):351-354
个性服务
 推荐该条目
 保存到收藏夹
 查看访问统计
 Endnote导出
Google Scholar
 Google Scholar中相似的文章
 [Zhang YH]的文章
 [Lu LW]的文章
 [Zhang MH]的文章
CSDL跨库检索
 CSDL跨库检索中相似的文章
 [Zhang YH]的文章
 [Lu LW]的文章
 [Zhang MH]的文章
Scirus search
 Scirus中相似的文章
Social Bookmarking
  Add to CiteULike  Add to Connotea  Add to Del.icio.us  Add to Digg  Add to Reddit 
所有评论 (0)
暂无评论

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。

 

 

Valid XHTML 1.0! 版权所有 © 2007-2012  中国科学院半导体研究所  -反馈
系统开发与技术支持:中国科学院国家科学图书馆兰州分馆(信息系统部)
本系统基于 MIT 和 Hewlett-Packard 的 DSpace 软件开发