题名: High-performance 1.55 mu m low-temperature-grown GaAs resonant-cavity-enhanced photodetector
作者: Han Q (Han Q.);  Niu ZC (Niu Z. C.);  Peng LH (Peng L. H.);  Ni HQ (Ni H. Q.);  Yang XH (Yang X. H.);  Du Y (Du Y.);  Zhao H (Zhao H.);  Wu RH (Wu R. H.);  Wang QM (Wang Q. M.)
发表日期: 2006
摘要: A 1.55 mu m low-temperature-grown GaAs (LT-GaAs) photodetector with a resonant-cavityenhanced structure was designed and fabricated. A LT-GaAs layer grown at 200 degrees C was used as the absorption layer. Twenty- and fifteen-pair GaAs/AlAs-distributed Bragg reflectors were grown as the bottom and top mirrors. A responsivity of 7.1 mA/W with a full width at half maximum of 4 nm was obtained at 1.61 mu m. The dark current densities are 1.28x10(-7) A/cm(2) at the bias of 0 V and 3.5x10(-5) A/cm(2) at the reverse bias of 4.0 V. The transient response measurement showed that the photocarrier lifetime in LT-GaAs is 220 fs. (c) 2006 American Institute of Physics.
KOS主题词: High-speed aeronautics;  social dominance
刊名: APPLIED PHYSICS LETTERS
专题: 中国科学院半导体研究所(2009年前)_期刊论文

条目包含的文件

文件 大小格式
3147.pdf65KbAdobe PDF 联系获取全文


许可声明:条目相关作品遵循知识共享协议(Creative Commons)。


推荐引用方式:
Han Q (Han Q.); Niu ZC (Niu Z. C.); Peng LH (Peng L. H.); Ni HQ (Ni H. Q.); Yang XH (Yang X. H.); Du Y (Du Y.); Zhao H (Zhao H.); Wu RH (Wu R. H.); Wang QM (Wang Q. M.) .High-performance 1.55 mu m low-temperature-grown GaAs resonant-cavity-enhanced photodetector ,APPLIED PHYSICS LETTERS,2006 ,89(13):Art.No.131104
个性服务
 推荐该条目
 保存到收藏夹
 查看访问统计
 Endnote导出
Google Scholar
 Google Scholar中相似的文章
 [Han Q (Han Q.)]的文章
 [Niu ZC (Niu Z. C.)]的文章
 [Peng LH (Peng L. H.)]的文章
CSDL跨库检索
 CSDL跨库检索中相似的文章
 [Han Q (Han Q.)]的文章
 [Niu ZC (Niu Z. C.)]的文章
 [Peng LH (Peng L. H.)]的文章
Scirus search
 Scirus中相似的文章
Social Bookmarking
  Add to CiteULike  Add to Connotea  Add to Del.icio.us  Add to Digg  Add to Reddit 
所有评论 (0)
暂无评论

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。

 

 

Valid XHTML 1.0! 版权所有 © 2007-2012  中国科学院半导体研究所  -反馈
系统开发与技术支持:中国科学院国家科学图书馆兰州分馆(信息系统部)
本系统基于 MIT 和 Hewlett-Packard 的 DSpace 软件开发